High Aluminum White Fire Resistant Bricks , Sintered Mullite High Temperature Brick

Categories Refractory Fire Bricks
Brand Name: KAMTAI
Model Number: KTMFB3
Certification: SGS
Place of Origin: CHINA
MOQ: 3000PCS
Price: Negotiable
Payment Terms: L/C, T/T, Western Union, MoneyGram,Paypal
Supply Ability: 50000PCS / MONTH
Delivery Time: 25 DAYS AFTER PAYMENT
Packaging Details: PLYWOOD PALLET
Material:: Mullite
Al2O3 Content: 65%
SiO2 content: 32%
Standard size: 230*114*65mm
Density: 0.6-1g/cm3
Feature: Thermal shock
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    High Aluminum White Fire Resistant Bricks , Sintered Mullite High Temperature Brick

    Lightweight insulating mullite brick white Insulating Refractory fire Brick

    1. Description

    In mullite (3 2 sio2, al2o3) phase of high aluminum refractory material. General alumina content is between 65% ~ 75%. Mineral composition in addition to the mullite, contain the alumina lower also contains a small amount of glass phase and cristobalite; Containing alumina high contains a small amount of corundum.High refractoriness, can reach more than 1790 ℃. The rul start temperature of 1600 ~ 1700 ℃. Room temperature compressive strength of 70 ~ 260 mpa. Good thermal shock resistance. A sintered mullite bricks and two fused mullite brick.

    Sintered mullite brick with high bauxite clinker as the main raw material, add a small amount of clay or raw bauxite as binder, forming, sintering and made. Fused mullite brick with high alumina, alumina industry and refractory clay as raw material, adding charcoal or coke fine as a reducing agent, reduction fused method is used to manufacture after forming.

    2. Feature

    Mullite insulating bricks characteristics and advantages: 1. Lower content of iron, alkaline and impurities, good high temperature properties. 2. Homogeneous structure, light weight, energy saving because lower heat storage in the furnace during cooling cycles. 3. High strength, good thermal shock resistance under high temperature. 4. Precise sizes due to grinding and shaping after sintering, which meets the requirement of construction. 5. Max service temp: Up to 1730C (3160F)

    3. Technical data
    Index /brand2326283032
    Classification temperature/ºC12601430154016501760
    Bulk density kg/m 358080095010301250
    Moudulus of rupture MPa0.
    Cold crushing strength MPa1.
    Permanent Liner Change % C xHr-0.1-0.5-0.8-0.9-0.9
    Thermal expansion coefficient ( 1100 C ) %0.450.500.550.600.65
    Thermal conductivity (W/m.k)400 C0.170.240.300.400.49
    600 C0.190.270.320.420.50
    800 C0.220.300.350.440.51
    1000 C0.250.320.380.450.53
    1200 C0.350.390.470.55
    Al2O3 %3850647276
    Fe2O3 %
    SiO2 %524333260.4
    TiO2 %
    CaO+ MgO %
    K2O+ Na2O %

    It is mainly used for hot blast stove top, blast furnace and furnace bottom, the regenerator of glass furnace, ceramic sintering kiln, petroleum cracking system corner lining, etc. Also widely used in hot blast stove, metal furnace, ceramic tunnel kilnelectrical porcelain shuttle kiln, etc., has a broad market prospect.

    4. Pacakge

    Package: The bricks are always palletized and shrink wrapped, usually 1.2~1.5MT per pallet.

    Shipping: Delivery by sea or as customer requirment.

    Departure Port : Shanghai port or as requirment.

    Quality High Aluminum White Fire Resistant Bricks , Sintered Mullite High Temperature Brick for sale