OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

Battery Wrapping Flame Barrier Films High flame retardant silicone rubber battery thermal wrap

Main Features

It is used to realize buffering energy absorption between battery pack cells.

Jelly Roll Insulation
Top Cap Insulation
Separator Papers
Tab & Lead insulation
Pouches
Thermal Insulation
Thermal Runaway Protection
Go-Therm Thermal Runaway Barrier

Specification

The main performance parameters are shown in Table

Serial number	Test items	Unit	Test Standard	SR No.
Serial number	Test items	Unit	Test Standard	SR 35-A	SR 40-A	SR 50-A	SR 60-A
1	Hardness	Shore A	GB/T531.1-2008	35±7	40±10	50±10	60±10
2	Density	g/cm3	4.3.2	0.8≤μ±3σ≤1.4	1.00≤μ±3σ≤1.51	1.00≤μ±3σ≤1.51	1.1≤μ±3σ≤1.5
3	25℃ Compression curve	MPa	GB/T 7757-2009	10%:0.12≤μ±3σ≤0.22	10%:0.25≤μ±3σ≤0.53	10%:0.25≤μ±3σ≤0.75	10%: 0.45≤μ±3σ≤0.80
				20%:0.25≤μ±3σ≤0.45	20%:0.50≤μ±3σ≤0.86	20%:0.63≤μ±3σ≤1.77	20%: 0.95≤μ±3σ≤1.45
				30%:0.45≤μ±3σ≤0.7	30%:0.68≤μ±3σ≤1.32	30%:1.20≤μ±3σ≤2.24	30%: 1.50≤μ±3σ≤2.50
4	25℃ Shear performance under pressure			Strength: µ-3σ≥0.8	Shear strength under pressure: µ-3σ≥0.5	Shear strength under pressure: µ-3σ≥0.2	Shear strength under pressure: µ-3σ≥0.8
4	25℃ Shear performance under pressure			Modulus: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75
5	25℃ Tensile strength	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
6	-30℃ Compression curve	MPa	GB/T 7757-2009	10%:0.08≤μ±3σ≤.0.22	10%:0.25≤μ±3σ≤0.53	10%:0.35≤μ±3σ≤0.65	10%:0.55≤μ±3σ≤0.90
				20%:0.25≤μ±3σ≤0.45	20%:0.50≤μ±3σ≤0.86	20%:0.90≤μ±3σ≤1.20	20%:1.10≤μ±3σ≤1.95
				30%:0.45≤μ±3σ≤0.9	30%:0.68≤μ±3σ≤1.32	30%:1.50≤μ±3σ≤2.00	30%: 2.00≤μ±3σ≤3.95
7	-30℃ Shear performance under pressure			Strength: µ-3σ≥0.8	Shear strength under pressure: µ-3σ≥0.5	Shear strength under pressure: µ-3σ≥0.2	Shear strength under pressure: µ-3σ≥0.8
7	-30℃ Shear performance under pressure			Modulus: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75
8	-30℃ Tensile strength	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
8	-30℃ Tensile strength	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
9	60℃ Compression curve	MPa	GB/T 7757-2009	10%:0.12≤μ±3σ≤0.22	10%:0.25≤μ±3σ≤0.53	10%:0.35≤μ±3σ≤0.70	10%: 0.35≤μ±3σ≤0.80
				20%:0.25≤μ±3σ≤0.45	20%:0.50≤μ±3σ≤0.86	20%:0.80≤μ±3σ≤1.30	20%:0.65≤μ±3σ≤1.60
				30%:0.45≤μ±3σ≤0.7	30%:0.68≤μ±3σ≤1.32	30%:1.00≤μ±3σ≤2.10	30%: 1.00≤μ±3σ≤2.50
10	60℃ Shear performance under pressure			Strength: µ-3σ≥0.8	Shear strength under pressure: µ-3σ≥0.5	Shear strength under pressure: µ-3σ≥0.2	Shear strength under pressure: µ-3σ≥0.8
10	60℃ Shear performance under pressure			Modulus: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75
11	60℃ Tensile strength	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
12	Double 85 post-aging compression curve	MPa	GB/T 7757-2009	10%:0.12≤μ±3σ≤0.22	10%:0.25≤μ±3σ≤0.53	10%: 0.50≤μ±3σ≤0.70	10%: 0.40≤μ±3σ≤1.90
				20%:0.25≤μ±3σ≤0.45	20%:0.50≤μ±3σ≤0.86	20%: 0.90≤μ±3σ≤1.30	20%: 1.00≤μ±3σ≤3.20
				30%:0.45≤μ±3σ≤0.75	30%:0.68≤μ±3σ≤1.32	30%: 1.40≤μ±3σ≤2.10	30%: 1.70≤μ±3σ≤5.50
13	Double 85 post-aging shear performance under pressure			Strength: µ-3σ≥0.8	Shear strength under pressure: µ-3σ≥0.5	Shear strength under pressure: µ-3σ≥0.2	Shear strength under pressure: µ-3σ≥0.8
13	Double 85 post-aging shear performance under pressure			Modulus: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75
14	Double 85 post-ageing Tensile strength	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
15	Compression curve after high and low-temperature cycle	MPa	GB/T 7757-2009	10%:0.12≤μ±3σ≤0.22	10%:0.25≤μ±3σ≤0.53	10%: 0.45≤μ±3σ≤0.65	10%: 0.50≤μ±3σ≤2.20
				20%:0.25≤μ±3σ≤0.45	20%:0.50≤μ±3σ≤0.86	20%: 0.85≤μ±3σ≤1.35	20%: 1.00≤μ±3σ≤4.00
				30%:0.45≤μ±3σ≤0.7	30%:0.68≤μ±3σ≤1.32	30%: 1.30≤μ±3σ≤2.50	30%: 1.80≤μ±3σ≤6.80
16	Shear performance under pressure after high and low temperature	MPa	ASTM C273C /273M-16	Strength: µ-3σ≥0.8	Shear strength under pressure: µ-3σ≥0.5	Shear strength under pressure: µ-3σ≥0.2	Shear strength under pressure: µ-3σ≥0.8
16		MPa	ASTM C273C /273M-16	Modulus: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75	Shear modulus under pressure: Min≥0.75
17	Tensile strength after high and low-temperature cycle	MPa	GB/T 528-2009	µ-3σ≥0.8	µ-3σ≥1.1	µ-3σ≥1.65	/
18	Flame retardant	/	UL94	UL94 V0(2mm)	V0(t≥2mm)	V0(t≥2mm)	V0(t≥2mm)
					V1(1≤t＜2mm)	V1(1≤t＜2mm)	V1(1≤t＜2mm)
					HB(0.4≤t＜1mm)	HB(0.4≤t＜1mm)	HB(0.4≤t＜1mm)
19	Forbidden object	/	RoHS &REACH & ELV	RoHS &REACH & ELV	RoHS &REACH & ELV	RoHS &REACH & ELV	RoHS &REACH & ELV
20	Insulation	MΩ	1000V DC 60s	µ-3σ≥500	µ-3σ≥500	µ-3σ≥500	µ-3σ≥500
21	Impedance	mA	2700V DC 60s	µ+3σ≤1	µ+3σ≤1	µ+3σ≤1	µ+3σ≤1
22	Thermal conductivity	W/(m·K)	GB/T 10295-2008	µ+3σ≤0.8	µ+3σ≤0.8	µ+3σ≤0.8	µ+3σ≤0.8
23	Specific heat capacity	J/(g·K)	ASTM E1269-2011	µ-3σ≥0.9	µ-3σ≥0.9	µ-3σ≥0.9	µ-3σ≥0.9
24	Stress retention rate	%	GB/T1685-2008	≥40	≥40	≥40	≥40
25	25℃ Shear strength with double-sided adhesive	MPa	ASTM D1002	Min≥0.8	Min≥0.8	Min≥1.1	Min≥1.5
26	-30℃ Shear strength with double-sided adhesive	MPa	ASTM D1002	Min≥0.6	Min≥0.8	Min≥1.1	Min≥1.5
27	60℃ Shear strength with double-sided adhesive	MPa	ASTM D1002	Min≥0.6	Min≥0.8	Min≥0.6	Min≥1.5
28	Double 85 ageing shear strength with double-sided adhesive	MPa	ASTM D1002	Min≥0.6	Min≥0.8	Min≥1.1	Min≥1.5
29	Shear strength after high and low-temperature cycles with double-sided adhesive	MPa	ASTM D1002	Min≥0.6	Min≥0.8	Min≥1.1	Min≥1.5
29		MPa	ASTM D1002	Min≥0.6	Min≥0.8	Min≥1.1	Min≥1.5

Available in – Continuous rolls or cut sheets
Durometers available – 70
Thicknesses available (in) – 0.0625 to 0.25
Typical roll lengths (ft) – 50 to 100
Typical roll widths (in) – 36 & 48
Surface finishing – Smooth finish, both sides
Color – Black

Typical Applications

Ev Battery Pack Structure is Fireproof and Insulated;
Aerospace Cargo Fire Covers;
A Protective Layer of the Brake Line of Railway Vehicles;
Fire Barrier Between Railway Passenger Cars.

Package & Delivery

Product Tags:

ODM Battery Thermal Wrap

Electrically Conductive Silicone Rubber Sheet

Flame Barrier Silicone Rubber Sheet

OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Fuzhou Fuqiang Precision Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Categories	Battery Thermal Wrap
Brand Name:	FQ
Model Number:	Rubber 1
Certification:	IATF16949
Place of Origin:	China
MOQ:	Customized
Price:	Fuzhou Fuqiang Precision Co.,Ltd.
Payment Terms:	L/C, T/T, D/P
Supply Ability:	1000pcs/day
Delivery Time:	1000 pcs/ days
Packaging Details:	pp bag+Cartons
Material:	High flame retardant silicone rubber(buffer frame)
Temperature Range:	-50°C to +240°C (continuous)
Color:	Gray
Sample:	Available

OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

ODM Battery Thermal Wrap

Electrically Conductive Silicone Rubber Sheet

Flame Barrier Silicone Rubber Sheet

OEM ODM Flame Barrier Electrically Conductive Silicone Rubber Sheet

Founded in 2005