| Brand Name: | Crystro |
| Model Number: | CR20200309-3 |
| Certification: | SGS |
| Place of Origin: | China |
| MOQ: | 1pc |
| Price: | Negotiable |
| Payment Terms: | T/T, Western Union, MoneyGram, Paypal |
| Supply Ability: | 1000pcs/month |
| Delivery Time: | 3-4 weeks |
| Packaging Details: | Carton Package |
| Polishing: | double side polished |
| Diameter: | 2''-3'' |
| Thickness: | 0.5mm/1mm |
| Surface finish: | < 10A |
| Type: | Round,Square,Flats |
| Orientation: | <100>,<111> |
| Coating: | AR Coating |
| Brand: | CRYSTRO |
| Company Info. |
| ANHUI CRYSTRO CRYSTAL MATERIALS Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
LSAT Single Crystal Substrates For Sale
(La,Sr)(Al,Ta)O3, LSAT is a relatively mature non-crystalline perovskite crystal. It has a perfect match with high temperature superconductors and various oxide materials. During a large number of practical researches, it was found that LSAT is promising to replace lanthanum aluminate (LaAlO3) and barium titanate (SrTiO3) for giant magnets and superconducting devices.
We supply (La,Sr)(Al,Ta)O3, LSAT substrate in various size and
orientation, Welcome to send us a inquiry for price and
specification of LSAT substrate.
| The main performance parameters | |
| Growth method | Czochralski method |
| Crystal structure | Cubic |
| Lattice constant | a = 3.868 A |
| Melting point (℃) | 1840 |
| Density | 6.74 (g / cm 3) |
| Hardness | 6.5 (mohs) |
| Permittivity | 22 |
| Thermal expansion coefficient | 10 x 10 -6 |
| Color and Appearance | Colorless to light brown, without crystal-twin |
| Standard Size | 10x3mm, 10x5mm, 10x10mm, 15x15mm, 20x15mm, 20x20mm, |
| Ф15mm, Ф20mm, Ф1"(25.4mm), Ф2"(50.8mm) | |
| Standard Thickness | 0.5mm, 1.0mm |
| Polishing | Single or double side polished |
| Crystal orientation | <100>, <110>, <111> ± 0.5 º |
| Ra: | ≤ 5Å (5μm × 5μm) |
| Package | 100 clean bag, 1000 clean room |
|
Round LaAlO3 Wafer Optical Substrate High Pressure Experimental Phase Double Side Polished
MgAl2O4 Magnesium Aluminate
Co2+:MgAl2O4 Single Crystal Substrate
YIG SGGG Substrates Wafer
Cubic SGGG Single Crystal
7.09 G/Cm3 EPI Polished 10x10x0.5mm GSGG Single Crystal
No Doped COC Czochralski 0.5mm Si Single Crystal Silicon Wafer
Low Optical Losses 7.09g/Cm3 Liquid Epitaxy Film SGGG Gd3Ga5O12
4inch Diameter 500µM Ggg Gadolinium Gallium Garnet Substrates
Substituted GGG SGGG EPI 1SP Single Crystal Substrates