UNS S32205 / S31803 Duplex Stainless Steel Plate Sheet Thickness 1.0 - 80.0mm Custom Cutting

2205 Duplex Stainless Steel: A Technical Overview

Chemical Makeup and Microstructural Advantage

• Chromium (Cr): 21–23% | Enhances passivity and resistance to general corrosion.
• Nickel (Ni): 4.5–6.5% | Stabilizes the austenitic phase for ductility and toughness.
• Molybdenum (Mo): 2.5–3.5% | Boosts resistance to pitting and crevice corrosion in chloride-rich media.
• Nitrogen (N): 0.08–0.20% | A key alloying element that strengthens the lattice, elevates yield strength, and further enhances corrosion resistance.
• Carbon (C): ≤0.03% | Minimizes carbide precipitation during welding, preserving ductility.

Mechanical Performance: Strength Meets Ductility

• Tensile Strength: ≥ 650 MPa | Nearly double that of 304 stainless steel.
• Yield Strength: ≥ 450 MPa | Enables thinner material designs without compromising structural integrity.
• Elongation: ≥ 25% | Maintains formability for complex fabrications.
• Impact Toughness: ≥ 100 J at 0°C | Resists brittle failure in low-temperature applications.

Corrosion Resistance: Tackling Aggressive Media

1. Pitting & Crevice Corrosion:
   • Superior in seawater, brine, and acidic solutions due to high Mo and N content.
   • Outperforms austenitic steels in stagnant or oxygen-deprived environments (e.g., heat exchangers with poor flow).
2. Stress Corrosion Cracking (SCC):
   • Resistant to chloride-induced SCC, a common failure mode in 300-series steels. This makes it suitable for offshore oil rigs, desalination plants, and chemical reactors.
3. Oxidative & Reductive Environments:
   • Stable in dilute sulfuric acid, phosphoric acid, and alkaline solutions, though concentrated acids may require higher-alloyed grades.

Fabrication and Welding Considerations

• Hot Working: Perform at 1050–1200°C to avoid phase imbalance; rapid cooling post-forming preserves the duplex structure.
• Cold Working: Feasible for sheets and tubes, but heavy deformation (e.g., deep drawing) may necessitate solution annealing at 1020–1100°C to prevent embrittlement.
• Welding:
  • Use filler metals like ER2209 (matching composition) to maintain phase balance.
  • Control heat input to < 1.5 kJ/mm to avoid excessive ferrite formation, which can reduce toughness.
  • Post-weld cooling should be rapid (e.g., water quenching for thin sections) to prevent sigma phase precipitation.

Industrial Applications: Where Performance Matters

• Oil & Gas:
  • Subsea pipelines, wellheads, and valves in high-salinity, H₂S-rich environments.
  • Offshore platforms exposed to seawater and atmospheric corrosion.
• Marine Engineering:
  • Ship hulls, propellers, and seawater handling systems (e.g., desalination plants).
  • Coastal structures enduring salt spray and tidal immersion.
• Chemical Processing:
  • Reactors for organic acids, chlorinated solvents, and petrochemical intermediates.
  • Heat exchangers in pharmaceutical and food-grade applications.
• Energy Sector:
  • Wet flue gas desulfurization (WFGD) systems in power plants.
  • Nuclear waste storage components requiring long-term corrosion resistance.

International Standards and Certification

• ASTM A240/A240M | Specifies plate, sheet, and strip.
• EN 10216-5 | Covers seamless tubes for pressure purposes.
• ASME SA-240 | Valid for boiler and pressure vessel applications.
• NACE MR0175 | Certified for use in sour gas environments (H₂S ≤ 3.5%).

Comparative Edge: Why Choose 2205 Over Other Alloys?