| Categories | FeCrAl Alloy |
|---|---|
| Brand Name: | DLX |
| Model Number: | 1Cr13Al4 |
| Place of Origin: | China Jiangsu |
| MOQ: | 5 |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 500 tons per month |
| Delivery Time: | 7-20 days |
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Material: | Ferrous Chromium Aluminum |
| Resistivity: | 1.25+/-0.05 |
| Tensile Strength: | 580-680MPA |
| Elongtation: | ≥12% |
| Application: | Heating, Resistivity |
| Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide |
| Maximum Temperature: | 950℃ |
| Melting Point: | 1450℃ |
| Certification: | CE,ROHS |
| Company Info. |
| Changzhou DLX Alloy Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
1Cr13Al4 alloy is a high resistance electric heating alloy, known for its excellent corrosion resistance and high-temperature strength. It has a high electrical resistivity and a low resistance temperature coefficient. The main components of 1Cr13Al4 include chromium, aluminum, nickel, etc., which endow the alloy with good electrical resistivity, high-temperature oxidation resistance, and corrosion resistance.
The application of 1Cr13Al4 resistance wire in electric heating devices is very extensive. They are usually used as heating elements, converting electrical energy into heat energy for heating air, liquids, or solids. This type of resistance wire has good electrical and mechanical properties, so it is widely used in many electric heating devices.
In household appliances, 1Cr13Al4 resistance wire is commonly used in ovens, electric stoves, water heaters, dryers, and other heating equipment. They can also be used to manufacture household heating devices such as fan heaters and electric heaters. In addition, in the industrial field, 1Cr13Al4 resistance wire is also widely used in industrial heating equipment such as heating furnaces, melting furnaces, and drying equipment.
One of the advantages of 1Cr13Al4 resistance wire is its stable resistance characteristics, which can maintain a stable resistance at high temperatures. This makes them very suitable for occasions requiring high-temperature heating. Additionally, 1Cr13Al4 resistance wire has good oxidation resistance and corrosion resistance, allowing it to work stably for a long time in harsh working environments.
Overall, the application of 1Cr13Al4 resistance wire in electric heating devices is extensive, capable of meeting the heating needs of different occasions, and is a high-performance and reliable heating element material.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
 | ||
 | ||
 | ||
 | ||
 | ||
|
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
0Cr23Al5 fecral 0cr25al5 Wire 1300 Degree 630 MPA Oxidized Wire Ribbon Resistohm 135
Bright 0Cr27Al7Mo2 830 MPA 2.5mmx180mm FeCrAl Alloy
0Cr21Al6 Toasters 0.03mm Iron Chromium Aluminum Alloy
630 MPA FeCrAl Alloy
0Cr21Al4 High Chrome Iron
0.5x5mm FeCrAl Alloy